Niobium (Columbium) (Annealed Sample)
Hardness, Vickers 80 Tensile Strength, Ultimate 300 MPa Tensile Strength, Yield 207 MPa Elongation at Break 30% Modulus of Elasticity 103 GPa Poisson's Ratio 0,38 Shear Modulus 37,5 GPa Niobium (Columbium) (Cold-Worked) Hardness, Brinell 126 Converted from Vickers for 3000 kg load/10 mm ball Brinell test Hardness, Rockwell A 45 Hardness, Rockwell B 71 Hardness, Vickers 130 Tensile Strength, Ultimate 600 MPa Niobium (Columbium) (Wrought) Hardness, Brinell 152 Converted from Vickers for 3000 kg load/10 mm ball Brinell test Hardness, Knoop 175 Hardness, Rockwell B 81,7 Hardness, Vickers 160 Tensile Strength, Ultimate 585 MPa Elongation at Break 5%
Molybdenum (Annealed) Hardness, Brinell 225 Converted from Vickers for 3000 kg load/10 mm ball Brinell test Hardness, Rockwell A 60 Converted from Vickers Hardness, Rockwell B 98 Converted from Vickers Hardness, Rockwell C 19 Converted from Vickers Hardness, Vickers 230 Tensile Strength, Ultimate 324 MPa Tensile Strength, Ultimate 350 MPa Single crystal Modulus of Elasticity 330 GPa; 275 GPa at 1000°C Compressive Yield Strength 400 MPa 0,01% Yield Bulk Modulus 272 GPa Shear Modulus 120 GPa Shear Strength 500 MPa torsional strain rate 0,25/sec Molybdenum (Recrystallized) Tensile Strength, Ultimate 415 MPa Tensile Strength, Yield 300 MPa 0,2% Offset Elongation at Break Max 40% in 50 mm Molybdenum (Stress Relieved Condition) Tensile Strength, Ultimate 515 MPa Tensile Strength, Yield 415 MPa 0,2% Offset Elongation at Break 2–17% in 50 mm
Technetium (Annealed) Hardness, Brinell 112 Hardness, Vickers 151 Tensile Strength, Ultimate 800 MPa Tensile Strength, Yield 320 MPa 0,2% offset Elongation at Break 30% in 25 mm Modulus of Elasticity 322 GPa in tension Bulk Modulus 281 GPa Poisson's Ratio 0,31 Shear Modulus 123 GPa Technetium (As-Rolled) Hardness, Brinell 442 Hardness, Vickers 394 Tensile Strength, Ultimate 1510 MPa Tensile Strength, Yield 1290 MPa 0,2% offset Elongation at Break 4% in 25 mm
Ruthenium (Annealed) Hardness, Brinell 220 Converted from Vickers for 3000 kg load/10 mm ball Brinell test Hardness, Rockwell A 60 Converted from Vickers Hardness, Rockwell B 96 Converted from Vickers Hardness, Rockwell C 18 Converted from Vickers Hardness, Vickers 220 Tensile Strength, Ultimate 370 MPa Modulus of Elasticity 414 GPa Ruthenium (Hot Rolled Bar) Tensile Strength, Ultimate 540 MPa Modulus of Elasticity 414 GPa
Rhodium (Annealed) Hardness, Brinell 89 Converted from Vickers for 500 kg load/10 mm ball Brinell test Hardness, Rockwell A 35 Converted from Vickers Hardness, Rockwell B 51 Converted from Vickers Hardness, Vickers 100 Tensile Strength, Ultimate 951 MPa Modulus of Elasticity 359 GPa Rhodium (As-Plated) Hardness, Brinell 722 Converted from Vickers for 3000 kg load/10 mm ball Brinell test Hardness, Rockwell A 83 Converted from Vickers Hardness, Rockwell C 63 Converted from Vickers Hardness, Vickers 800 Tensile Strength, Ultimate 700 MPa Rhodium (Hardened) Tensile Strength, Ultimate 2068 MPa
Palladium Hardness, Vickers 37 Annealed Tensile Strength, Ultimate 180 MPa Annealed Modulus of Elasticity 117 GPa Poisson's Ratio 0,39 Shear Modulus 49 GPa Calculated
Silver Hardness, Vickers 25 Annealed Tensile Strength, Ultimate 140 MPa Annealed Modulus of Elasticity 76 GPa Poisson's Ratio 0,37 Annealed Poisson's Ratio 0,39 Hard drawn Shear Modulus 32 GPa Calculated; Annealed
Cadmium Hardness, Brinell 16–24 Hardness, Vickers 22 Tensile Strength, Ultimate 75 MPa Elongation at Break 50% in 25 mm Modulus of Elasticity 55,2 GPa Poisson's Ratio 0,33 Shear Modulus 19,2 GPa
Indium Hardness, Brinell 0,9 Hardness, Vickers Max 10 Tensile Strength, Ultimate 4,5 MPa Annealed Modulus of Elasticity 12,7 GPa in tension Compressive Yield Strength 2,14 MPa Poisson's Ratio 0,4498 Shear Modulus 5 GPa Calculated
Tin Hardness, Brinell 3,9 Tensile Strength, Ultimate 220 MPa Modulus of Elasticity 41,4 GPa Poisson's Ratio 0,33 Shear Modulus 18 GPa Calculated
Antimony Hardness, Brinell 30–58 Hardness, Vickers 30–60 Tensile Strength, Ultimate 11,4 MPa Modulus of Elasticity 77,759 GPa Shear Modulus 19 GPa
Tellurium Hardness, Brinell 25 Tensile Strength, Ultimate 11 MPa Modulus of Elasticity 40 GPa Poisson's Ratio 0,33 Shear Modulus 15,16 GPa
Cesium Bulk Modulus 1,57 GPa
Barium Modulus of Elasticity 12,8 GPa Bulk Modulus 10,2 GPa Poisson's Ratio 0,28 Shear Modulus 6 GPa Calculated
Lanthanum Hardness, Vickers 28 Tensile Strength, Ultimate 130 MPa Tensile Strength, Yield 125 MPa Elongation at Break 7,9% Modulus of Elasticity 36,6 GPa in tension Bulk Modulus 27,9 GPa Poisson's Ratio 0,28 Shear Modulus 14,3 GPa
Cerium Hardness, Vickers 24 Tensile Strength, Ultimate 100 MPa Tensile Strength, Yield 91 MPa Modulus of Elasticity 41,4 GPa Bulk Modulus 21,5 GPa Poisson's Ratio 0,248 Shear Modulus 13,5 GPa
Praseodymium Hardness, Vickers 20 Tensile Strength, Ultimate 110 MPa Tensile Strength, Yield 100 MPa Elongation at Break 15% Modulus of Elasticity 37,3 GPa in tension Bulk Modulus 28,8 GPa Poisson's Ratio 0,281 Shear Modulus 14,8 GPa
Neodymium Hardness, Vickers 18 Tensile Strength, Ultimate 170 MPa Tensile Strength, Yield 165 MPa Elongation at Break 25% Modulus of Elasticity 41,4 GPa Bulk Modulus 31,8 GPa Poisson's Ratio 0,281 Shear Modulus 16,3 GPa
Promethium Hardness, Knoop 63 Tensile Strength, Ultimate 160 MPa Tensile Strength, Yield 70 MPa Elongation at Break 25% Modulus of Elasticity 50 GPa (tension) Bulk Modulus 33 GPa Poisson's Ratio 0,28 Shear Modulus 18 GPa
Samarium Hardness, Vickers 39 Tensile Strength, Ultimate 120–156 MPa different sources report in this range Tensile Strength, Yield 68–112 MPa Elongation at Break 17% Modulus of Elasticity 49,7 GPa in tension Bulk Modulus 37,8 GPa Poisson's Ratio 0,274 Shear Modulus 19,5 GPa
Europium Hardness, Vickers 17 Modulus of Elasticity 18,2 GPa in tension Bulk Modulus 8,3 GPa Poisson's Ratio 0,152 Shear Modulus 7,9 GPa
Gadolinium Hardness, Vickers 37 polycrystalline Tensile Strength, Ultimate 190 MPa Tensile Strength, Yield 173 MPa Elongation at Break 37% Modulus of Elasticity 54,8 GPa in tension Bulk Modulus 37,9 GPa Poisson's Ratio 0,259 Shear Modulus 24 GPa Calculated
Terbium Hardness, Vickers 38 polycrystalline Tensile Strength, Ultimate 140 MPa Tensile Strength, Yield 60 MPa Elongation at Break 12% Modulus of Elasticity 55,7 GPa in tension Bulk Modulus 38,7 GPa Poisson's Ratio 0,26 Calculated Shear Modulus 22,1 GPa
Dysprosium Hardness, Vickers 44 Tensile Strength, Ultimate 246 MPa Tensile Strength, Yield 225 MPa Elongation at Break 30% Modulus of Elasticity 61,4 GPa in tension Bulk Modulus 40,5 GPa Poisson's Ratio 0,237 Shear Modulus 24,7 GPa
Holmium Hardness, Vickers 46 Tensile Strength, Ultimate 259 MPa Tensile Strength, Yield 221 MPa Modulus of Elasticity 64,8 GPa in tension Bulk Modulus 40,2 GPa Poisson's Ratio 0,231 Shear Modulus 26,3 GPa
Erbium Hardness, Vickers 42 Tensile Strength, Ultimate 136 MPa Tensile Strength, Yield 60 MPa Elongation at Break 11,5% Reduction of Area 11,9% Modulus of Elasticity 69,9 GPa in tension Bulk Modulus 44,4 GPa Poisson's Ratio 0,237 Shear Modulus 28,3 GPa
Thulium Hardness, Vickers 48 Tensile Strength, Ultimate 140 MPa Tensile Strength, Yield 60 MPa Elongation at Break 12% Modulus of Elasticity 74 GPain tension Bulk Modulus 44,5 GPa Poisson's Ratio 0,213 Shear Modulus 30,5 GPa
Ytterbium Hardness, Vickers 17 Tensile Strength, Ultimate 72 MPa Tensile Strength, Yield 66 MPa Elongation at Break 43% Modulus of Elasticity 23,7 GPa in tension Bulk Modulus 30,5 GPa Poisson's Ratio 0,207 Shear Modulus 9,9 GPa
Lutetium Hardness, Vickers 44 Tensile Strength, Ultimate 140 MPa Tensile Strength, Yield 60 MPa Elongation at Break 12% Modulus of Elasticity 68,6 GPa in tension Bulk Modulus 47,6 GPa Poisson's Ratio 0,261 Shear Modulus 27,2 GPa
Hafnium (Rod) Tensile Strength, Ultimate 485 MPa Tensile Strength, Yield 240 MPa Elongation at Break 25% Hafnium (Plate) Tensile Strength, Ultimate 450 MPa Longitudinal Tensile Strength, Ultimate 470 MPa Transverse Tensile Strength, Yield 195 MPa Longitudinal Tensile Strength, Yield 310 MPa Transverse Elongation at Break 25% Longitudinal or Transverse Hafnium (Strip) Tensile Strength, Ultimate 450 MPa Longitudinal or Transverse Tensile Strength, Yield 170 MPa Longitudinal Tensile Strength, Yield 275 MPa Transverse Elongation at Break 30% Longitudinal or Transverse
Tantalum (Annealed) Hardness, Brinell 95 Converted from Vickers for 3000 kg load/10 mm ball Brinell test Hardness, Rockwell A 35 Converted from Vickers Hardness, Rockwell B 51 Converted from Vickers Hardness, Vickers 100 Tensile Strength, Ultimate 450 MPa Modulus of Elasticity 186 GPa Poisson's Ratio 0,35 Fatigue Strength 230 MPa 50,000,000 cycles, E-beam melted sample; rotating beam test, Shear Modulus 69 GPa
Популярное: Почему двоичная система счисления так распространена?: Каждая цифра должна быть как-то представлена на физическом носителе... Почему люди поддаются рекламе?: Только не надо искать ответы в качестве или количестве рекламы... Организация как механизм и форма жизни коллектива: Организация не сможет достичь поставленных целей без соответствующей внутренней... Генезис конфликтологии как науки в древней Греции: Для уяснения предыстории конфликтологии существенное значение имеет обращение к античной... ©2015-2024 megaobuchalka.ru Все материалы представленные на сайте исключительно с целью ознакомления читателями и не преследуют коммерческих целей или нарушение авторских прав. (195)
|
Почему 1285321 студент выбрали МегаОбучалку... Система поиска информации Мобильная версия сайта Удобная навигация Нет шокирующей рекламы |